Material:P3HT
Poly(3-hexylthiophene) (P3HT) is a polymer with chemical formula (C10H14S)n. It is a polythiophene with a short alkyl group on each repeat unit. It is noteworthy since it is a seminconducting polymer; it can conduct positive charges (holes). It is a common material for studies of organic electronics (e.g. FETs) and for organic photovoltaics (OPV).
Contents
Organization
P3HT typically organizes into a semi-crystalline state, with an idealized unit cell as shown below:
- The lamellar stacking has a spacing of ~1.6 nm, giving rise to a peak (100) at q ~0.4 Å−1.
- The aromatic (π-π) stacking has a spacing of ~0.39 nm, giving rise to a peak (010) at q ~1.6 Å−1.
- The spacing along the ring direction is too disordered to give a well-defined 001 peak.
Refer to P3HT orientation for details about the organization of P3HT.
Scattering
On flat substrates, P3HT typically organizes into an edge-on orientation, wherein the lamellar stacking direction is along the film normal (leading to the 100 peak being along qz), and the aromatic stacking then being in-plane (010 peak along qr).
Properties
- Density: ~1.33 g/cm3
- Neutron SLD: 0.817×10−6 Å−2
Material | density (g/cm3) | X-ray energy (keV) | X-ray wavelength (Å) | critical angle (°) | qc (Å−1) | SLD (10−6Å−2) |
---|---|---|---|---|---|---|
P3HT | 1.33 | 2.0 | 6.20 | 0.700 | 0.0248 | 12.20 |
4.0 | 3.10 | 0.352 | 0.0249 | 12.33 | ||
8.0 | 1.55 | 0.176 | 0.0249 | 12.29 | ||
12.0 | 1.03 | 0.117 | 0.0248 | 12.25 | ||
16.0 | 0.77 | 0.088 | 0.0248 | 12.24 | ||
24.0 | 0.52 | 0.058 | 0.0248 | 12.2 |